In ongoing research at the University of Idaho, potential failure mechanisms of airbag initiators are being investigated. Cracking of the cylindrical glass-to-metal seal (GTMS) present in these devices has been observed. These cracks could be a path for moist gas to diffuse into the initiator, potentially leading to bridge-wire degradation and late-fire or no-fire initiator failure. Previous research has shown that cracking may be caused by thermal stresses induced by the GTMS formation process. The goal of this research was to determine if welding of the output-can onto the initiator header could produce stresses in the glass great enough to cause cracking. A finite element analysis solution was chosen to model the transient heat transfer and temperature distribution in the initiator assembly during the welding process. The thermal stresses were calculated with a mechanical analysis once the temperature distribution was determined. Compressive stresses induced by pressing the header assembly into the output-can as part of the manufacturing process were also investigated with a closed-form mechanics of materials solution. The welding thermal stress model initially predicted radial stresses greater than the tangential stresses. This conflicts with observed radial cracks, which would be induced by tangential stresses. Subsequent investigations with an interface region stiffness model showed that when the stiffness of the bond at the pin-glass and glass-header interfaces is decreased, the maximum radial stress is greatly reduced and that the maximum tangential stress stays relatively constant. These predicted stresses were still in excess of the range of glass strengths reported in literature. However, superposition of the compressive stresses due to the press-fit and residual stresses created when the GTMS is formed with these thermal stresses results in the total radial and tangential stresses being on the same order as the reported strengths. It was determined that when initiators are overheated during welding, radial stresses due to thermal expansion cause the bond to fail and separation to occur over a portion of the pin-glass interface. Tangential stresses developed for the same reason are sufficient enough to cause radial cracking, where the bond is still intact.
Skip Nav Destination
e-mail: mmaughan@vandals.uidaho.edu
Article navigation
March 2009
Research Papers
Thermal Stresses Due to Laser Welding in Bridge-Wire Initiators
Michael R. Maughan,
Michael R. Maughan
Graduate Student
Department of Mechanical Engineering,
e-mail: mmaughan@vandals.uidaho.edu
University of Idaho
, Moscow, ID 83844
Search for other works by this author on:
Robert R. Stephens,
Robert R. Stephens
Professor
Department of Mechanical Engineering,
University of Idaho
, Moscow, ID 83844
Search for other works by this author on:
Donald M. Blackketter,
Donald M. Blackketter
Professor
Department of Mechanical Engineering,
University of Idaho
, Moscow, ID 83844
Search for other works by this author on:
Karl K. Rink
Karl K. Rink
Associate Professor
Department of Mechanical Engineering,
University of Idaho
, Moscow, ID 83844
Search for other works by this author on:
Michael R. Maughan
Graduate Student
Department of Mechanical Engineering,
University of Idaho
, Moscow, ID 83844e-mail: mmaughan@vandals.uidaho.edu
Robert R. Stephens
Professor
Department of Mechanical Engineering,
University of Idaho
, Moscow, ID 83844
Donald M. Blackketter
Professor
Department of Mechanical Engineering,
University of Idaho
, Moscow, ID 83844
Karl K. Rink
Associate Professor
Department of Mechanical Engineering,
University of Idaho
, Moscow, ID 83844J. Electron. Packag. Mar 2009, 131(1): 011009 (8 pages)
Published Online: February 13, 2009
Article history
Received:
July 30, 2007
Revised:
August 10, 2008
Published:
February 13, 2009
Citation
Maughan, M. R., Stephens, R. R., Blackketter, D. M., and Rink, K. K. (February 13, 2009). "Thermal Stresses Due to Laser Welding in Bridge-Wire Initiators." ASME. J. Electron. Packag. March 2009; 131(1): 011009. https://doi.org/10.1115/1.3068318
Download citation file:
Get Email Alerts
Cited By
Anand Model Constants of Sn–Ag–Cu Solders: What Do They Actually Mean?
J. Electron. Packag (June 2025)
Sequential Versus Concurrent Effects in Combined Stress Solder Joint Reliability
J. Electron. Packag (June 2025)
Related Articles
Welding of Alumina Using a Pulsed Dual-Beam CO 2 Laser
J. Manuf. Sci. Eng (February,2011)
Nonlinear Viscoelastic Finite Element Analysis of Physical Aging in an Encapsulated Transformer
J. Electron. Packag (March,2009)
Finite Element Predictions of Temperature Distributions in a Multipass Welded Piping Branch Junction
J. Pressure Vessel Technol (February,2005)
Numerical Simulations and Experimental Results of Tensile Test Behavior of Laser Butt Welded DP980 Steels
J. Eng. Mater. Technol (October,2008)
Related Proceedings Papers
Related Chapters
Defining Joint Quality Using Weld Attributes
Ultrasonic Welding of Lithium-Ion Batteries
Introduction
Ultrasonic Welding of Lithium-Ion Batteries
Concluding Remarks and Future Work
Ultrasonic Welding of Lithium-Ion Batteries