Segmented chips are known to form in machining of titanium alloys due to localization of heat in the shear zone, which is a function of machining environment. To investigate the correlation between machining environments and microstructural aspects of chip segmentation, orthogonal turning experiments were performed under three machining environments, viz., room, LN2, and 260 °C. Scanning electron and optical microscopy of chip roots show that the mechanism of chip segment formation changes from plastic strain and mode II fracture at room temperature, to predominant mode I fracture at LN2 and plastic strain leading to shear band formation at 260 °C. The chip segment pitch and shear plane length predicted using Deform™ matched well with the experimental values at room temperature. The microstructural analysis of chips show that higher shear localization occurs at room temperature than the other two temperatures. The depth of machining affected zone (MAZ) on work surfaces was lower at the two temperatures than that of at the room temperature at a higher cutting speed of 91.8 m/min.
Microstructural Characterization of Chip Segmentation Under Different Machining Environments in Orthogonal Machining of Ti6Al4V
Contributed by the Materials Division of ASME for publication in the JOURNAL OF ENGINEERING MATERIALS AND TECHNOLOGY. Manuscript received January 8, 2014; final manuscript received October 9, 2014; published online November 7, 2014. Assoc. Editor: Toshio Nakamura.
- Views Icon Views
- Share Icon Share
- Search Site
Joshi, S., Tewari, A., and Joshi, S. S. (January 1, 2015). "Microstructural Characterization of Chip Segmentation Under Different Machining Environments in Orthogonal Machining of Ti6Al4V." ASME. J. Eng. Mater. Technol. January 2015; 137(1): 011005. https://doi.org/10.1115/1.4028841
Download citation file: