Abstract

Structural integrity assessment of reactor pressure vessels (RPVs) is essential for the safe operation of nuclear power plants. For RPVs in pressurized water reactors (PWRs), the assessment should be performed by considering neutron irradiation embrittlement and pressurized thermal shock (PTS) events. To assess the structural integrity of an RPV, a traditional method is usually employed by comparing fracture toughness of the RPV material with the stress intensity factor (KI) of a crack postulated near the RPV inner surface. When an underclad crack (i.e., a crack beneath the cladding of an RPV) is postulated, KI of this crack can be increased owing to the plasticity effect of cladding. This is because the yield stress of cladding is lower than that of base metal and the cladding may yield earlier than base metal. In this paper, detailed three-dimensional (3D) finite element analyses (FEAs) were performed in consideration of the plasticity effect of cladding for underclad cracks postulated in Japanese RPVs. Based on the 3D FEA results, a plasticity correction method was proposed on KI calculations of underclad cracks. In addition, the effects of RPV geometries and loading conditions were investigated using the proposed plasticity correction method. Moreover, the applicability of the proposed method to the case which considers the hardening effect of materials after neutron irradiation was also investigated. All of these results indicate that the proposed plasticity correction method can be used for KI calculations of underclad cracks and is applicable to structural integrity assessment of Japanese RPVs containing underclad cracks.

References

1.
Japan Electric Association
,
2016
, “
Nuclear Standards Committee of JEA, Method of Verification Tests of the Fracture Toughness for Nuclear Power Plant Components
,” Japan Electric Association, Tokyo, Japan, Standard No. JEAC4206-2016 (in Japanese).
2.
Moinereau
,
D.
,
Bezdikian
,
G.
, and
Faidy
,
C.
,
1999
, “
Three-Dimensional Analyses of Shallow Subclad Flaws in a PWR Vessel Submitted to a Severe Overcooling Transient
,”
Fracture, Design Analysis of Pressure Vessels, Heat Exchangers, Piping Components, and Fitness for Service
, ASME PVP, New York, Vol.
388
, pp.
45
60
.https://www.tib.eu/en/search/id/BLCP%3ACN033029020/Three-Dimensional-Analyses-of-Shallow-Subclad-Flaws/
3.
French Association for Design
,
2010
, “
In-Service Inspection Rules for Mechanical Components of PWR Nuclear Islands
,”
French Association for Design
, Courbevoie, France, pp.
21
23
.https://inis.iaea.org/search/search.aspx?orig_q=RN:49023868
4.
Marie
,
S.
, and
Nédélec
,
M.
,
2007
, “
A New Plastic Correction for the Stress Intensity Factor of an Under-Clad Defect in a PWR Vessel Subjected to a Pressurised Thermal Shock
,”
Int. J. Pressure Vessels Piping
,
84
(
3
), pp.
159
170
.10.1016/j.ijpvp.2006.09.019
5.
Katsuyama
,
J.
,
Huang
,
L.
,
Li
,
Y.
, and
Onizawa
,
K.
,
2015
, “
Effects of Plasticity on the Stress Intensity Factor Evaluation for Underclad Crack Under Pressurized Thermal Shock Events
,”
ASME
Paper No. PVP2015-45411. 10.1115/PVP2015-45411
6.
Dassault Systèmes Simulia Corp.
,
2015
, “
Abaqus User's Manual, Version 6.14
,” Dassault Systèmes Simulia Corp., Providence, RI.
7.
Izumi
,
F.
,
Horikami
,
K.
,
Kobayashi
,
K.
, and
Namatame
,
K.
,
1993
, “
Data List of Nuclear Power Plants in Japan—PWR Edition (1992)
,” Japan Atomic Energy Research Institute, Ibaraki, Japan, Report No.
JAERI-M-92-204
(in Japanese).https://jopss.jaea.go.jp/pdfdata/JAERI-M-92-204.pdf
8.
Katsuyama
,
J.
,
Nishikawa
,
H.
,
Udagawa
,
M.
,
Nakamura
,
M.
, and
Onizawa
,
K.
,
2013
, “
Assessment of Residual Stress Due to Overlay-Welded Cladding and Structural Integrity of a Reactor Pressure Vessel
,”
ASME J. Pressure Vessel Technol.
,
135
(
5
), p.
051402
.10.1115/1.4024617
9.
Japan Power Engineering and Inspection Corporation
,
1992
, “
Investigation Report of Reliability Verification Test for Weld Heat-Affected Zone: Pressurized Thermal Shock Test for Reactor Pressure Vessels
,” Japan Power Engineering and Inspection Corporation, Tokyo, Japan, Report No. JPEIC-1992 (in Japanese).
10.
Marie
,
S.
, and
Chapuliot
,
S.
,
2008
, “
Improvement of the Calculation of the Stress Intensity Factors for Underclad and Through-Clad Defects in a Reactor Pressure Vessel Subjected to a Pressurized Thermal Shock
,”
Int. J. Pressure Vessels Piping
,
85
(
8
), pp.
517
531
.10.1016/j.ijpvp.2008.02.006
11.
Iwata
,
K.
,
Tobita
,
T.
,
Takamizawa
,
H.
,
Chimi
,
Y.
,
Yoshimoto
,
K.
, and
Nishiyama
,
Y.
,
2016
, “
Specimen Size Effect on Fracture Toughness of Reactor Pressure Vessel Steel Following Warm Pre-Stressing
,”
ASME
Paper No. PVP2016-63795. 10.1115/PVP2016-63795
12.
Wolfram Research, Inc.
,
2015
, “
Mathematica 10.1
,” Wolfram Research, Champaign, IL.
13.
Tobita
,
T.
,
Udagawa
,
M.
,
Chimi
,
Y.
,
Nishiyama
,
Y.
, and
Onizawa
,
K.
,
2014
, “
Effect of Neutron Irradiation on the Mechanical Properties of Weld Overlay Cladding for Reactor Pressure Vessel
,”
J. Nucl. Mater.
,
452
(
1–3
), pp.
61
68
.10.1016/j.jnucmat.2014.04.035
14.
Sakamoto
,
H.
,
Hirota
,
T.
, and
Ogawa
,
N.
,
2016
, “
Study on Evaluation Procedure for Calculating the Stress Intensity Factor of Flaws Beneath RPV Cladding During Pressurised Thermal Shock Events by FE Analysis
,”
ASME
Paper No. PVP2016-63210. 10.1115/PVP2016-63210
You do not currently have access to this content.