The importance of steel cleanliness for the performance of tapered roller bearings has been clearly established and has led to on-going improvements in steel production methods. The presence of non-metallic impurities within the steel can result in hard/brittle inclusions that may serve as initiation sites for damage due to sub-surface rolling contact fatigue (RCF) if the inclusions lie within the near-race of the bearing components due to the high mechanical stress present. Current inspection standards define steel cleanliness with respect to bulk inclusion morphology, which limits inspection to a small area that may or may not be representative of the entire steel heat. In this presentation, ultrasonic surface wave methods are described for detecting subsurface inclusions directly on finished bearing inner and outer rings. We expand on our previous work to exploit the different inspection depths that can be achieved with different measurement frequencies. The impact of the different inspection depths is quantified through simulated service life testing with heavy axle loading conditions. For this study, bearing components were first subjected to ultrasonic surface wave testing at three different frequencies to identify near-race inclusions. The simulated service life testing was then used to assess the onset and propagation of RCF failure. RCF spall initiations correlated highly with the positions identified by the ultrasonic inspections suggesting that this approach has a predictive potential. However, additional research is needed to establish the specific criteria needed for such predictions with respect to the inclusion location along the race, the depth from the race surface, the inclusion morphology and the inclusion mechanical properties. This work is anticipated to improve the understanding of RCF damage initiation which will lead a higher level of safety for railroad operations.

Bearing steel cleanliness is directly linked to failures caused by the interaction of subsurface defects and rolling contact fatigue (RCF). Optical analysis of as-received steel coupled with ultrasonic inspection on finished components minimizes the occurrence of defects in the near race. While useful as a preventative measure, these methods do not ensure that critical areas of components subjected to RCF are free of defects that act as stress concentrators and contribute to premature failure. This presentation provides a brief summary of the current technology and standards utilized in the industry. The deficiencies of the current methods for the particular case at hand are identified and a surface wave scanning method is introduced. The development and production of reference parts for this type of scanning are then discussed. The production method entails both traditional electro-discharge machining (EDM) and femtosecond laser machining (FLM) on finished bearing components such that the reference part microstructure resembles that of a finished part. Experimental results utilizing surface wave scanning are given for two types of assembly-ready bearing components that are then subjected to realistic service loads and mileage to the point of failure. The results of the service life simulations are then correlated with surface wave scanning results and are shown to be in good agreement. This work is anticipated to impact any field in which components are subjected to RCF.

This paper discusses the benefits of using on-board hand brake sensors to determine whether a freight car hand brake is applied or released in service. Unreleased hand brakes are a significant source of wheel tread damage, which can lead to wheel removals, and in extreme cases can cause damage and derailments. Also, hand brake-related accidents are a significant cause of North American railroad accidents. Wheel tread damage and wayside wheel impact load detectors (WILD) are reviewed, along with AAR why made codes for wheel removals. Wheel failures and other wheel impact associated damage are discussed, along with operational considerations for hand brakes. Further, on-board sensors in general, and hand brake sensors in particular, are described in detail and service data from monitored cars is presented. Additionally, possible safety and operational improvements related to use of hand brake sensors are discussed, along with comments on the use of sensors to assist with proactive maintenance of freight cars.