Abstract

Previous investigations have demonstrated the principle and feasibility of quasi-hydrodynamic lubrication using powders. With conventional lubricants, the hydrodynamic behavior of a journal bearing can be summarized in the form of a plot of friction coefficient against a nondimensional load parameter, usually referred to as a Stribeck curve. One of the main features of the curve is that, as the thickness of the lubricant film increases, the friction coefficient initially decreases until it reaches a minimum and then increases due to shearing of the lubricant film. Previous tests on a three pad journal bearing using molybdenum disulfide powder as the lubricant showed that its friction/load characteristics followed the Stribeck form. The experimental work reported herein describes further tests carried out on a three-pad journal bearing to evaluate its thermal stability and long term wear characteristics using tungsten disulfide powder as the lubricant. Dry tungsten disulfide powder lubricant has been shown to provide excellent wear resistance. Its friction properties are similar to molybdenum disulfide but it can be used at much higher temperatures. Bearing tests were carried out at speeds up to 30,000 rpm and loads up to 236 N. Over the load/speed range stable thermal operation was achieved. From friction torque measurements it was found that the coefficient of friction for the bearing was essentially constant over the range of loads and speeds. Unlike liquids, powders have a limiting shear strength property. When the limiting shear stress is reached in a powder flow, the powder essentially shears along a plane and does not flow in a viscous manner. The constant friction coefficient seen with the tungsten disulfide powder suggests that the powder had a low limiting shear strength and that this dominated the operation of the bearing in the tests. The total accumulated test time was more than eighteen hours. Periodically, the test journal and bearing pads were inspected but there was no measurable wear or visible damage.

Issue Section:
Research Papers
Topics:
Journal bearings, Friction, Lubricants, Stress, Bearings, Tungsten, Flow (Dynamics), Molybdenum, Shear strength, Wear, Damage, Die cutting, Lubrication, Shear stress, Shearing (Deformation), Temperature, Thermal stability, Torque measurement, Wear resistance
1.
Heshmat
 
H.
,
1991
, “
The Rheology and Hydrodynamics of Dry Powder Lubrication
,”
STLE Tribology Transactions
, Vol.
34
, No.
3
, pp.
433
–
439
.
2.
Heshmat
 
H.
,
1992
a, “
The Quasi-Hydrodynamic Mechanism of Powder Lubrication—Part I: Lubricant Visualization
,”
Lubrication Engineering
, Vol.
48
, No.
2
, pp.
96
–
104
.
3.
Heshmat
 
H.
,
1992
b, “
The Quasi-Hydrodynamic Mechanism of Powder Lubrication—Part II: Lubricant Pressure Profile
,”
Lubrication Engineering
, Vol.
48
, No.
5
, pp.
373
–
383
.
4.
Heshmat, H., 1992c “Static and Dynamic Characteristics of High-Temperature, Powder-Lubricated Materials,” Interim Report for July 1987 to June 1990, Aero Propulsion and Power Directorate, Wright Laboratory, Air Force Systems Command, Wright Patterson Air Force Base, WL-TR-92–2050, June.
5.
Heshmat, H., 1994 “On the Theory of Quasi-Hydrodynamic Powder Lubrication with Dry Powder. Application to Development of High-Speed Journal Bearings for Hostile Environments,” presented at the 20th Leeds-Lyon Symposium on Tribology held at the Institut National des Sciences Appliquees de Lyon, France, September 7–10, 1993. Dissipative Process in Tribology, D. Dowson, C. M. Taylor, T. H. C. Childs, M. Godet, and G. Dalmaz, eds., Tribology Series 27, Elsevier Scientific Publishing Co., New York, pp. 45–64.
6.
Heshmat, H., and Brewe, D., 1994 “Performance of Powder-Lubricated Journal Bearings with MOS2 Powder: Experimental Study of Thermal Phenomena,” Presented at the ASME/STLE Joint Tribology Conference, Hawaii, October, and to be published in the ASME JOURNAL OF TRIBOLOGY.
7.
Heshmat
 
H.
,
Godet
 
M.
, and
Berthier
 
Y.
, 1994, “
On the Role and Mechanism of Dry Triboparticulate Lubrication
, Presented at the Solid Lubricants Session of the 1994 STLE Annual Meeting, Pittsburgh, Pennsylvania, May 2–5. Lubrication Engineering,
Journal of the STLE
, Vol.
51
, No.
7
, July,
1995
, pp.
557
–
564
.
8.
Murray
 
S. F.
, and
Calabrese
 
S. J.
,
1993
, “
Effect of Solid Lubricants on Low Speed Sliding Behavior of Silicon Nitride at Temperatures to 800°C
,”
Lubrication Engineering
, Vol.
49
, No.
12
, pp.
955
–
964
.
This content is only available via PDF.
Copyright © 1996
 by The American Society of Mechanical Engineers
You do not currently have access to this content.